Stamping Magnetic Shielding Precision Alloys Bright Surface For Luxury Watches 1J79 manufacturer from China Ohmalloy Material Co.,Ltd

Stamping Magnetic Shielding Precision Alloys Bright Surface For Luxury Watches

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: 1J79

Stamping Magnetic Shielding Precision Alloys Bright Surface For Luxury Watches
(Common Name: Ni79Mo4, E11c, mallo

Stamping Magnetic Shielding Precision Alloys Bright Surface For Luxury Watches

(Common Name: Ni79Mo4, E11c, malloy, permalloy, 79HM)

Ohmalloy-1J79 is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content. Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields. Commercial permalloy alloys typically have relative permeability of around 100,000, compared to several thousand for ordinary steel.

In addition to high permeability, its other magnetic properties are low coercivity, near zero magnetostriction, and significant anisotropic magnetoresistance. The low magnetostriction is critical for industrial applications, allowing it to be used in thin films where variable stresses would otherwise cause a ruinously large variation in magnetic properties. Permalloy's electrical resistivity can vary as much as 5% depending on the strength and the direction of an applied magnetic field. Permalloys typically have the face centered cubic crystal structure with a lattice constant of approximately 0.355 nm in the vicinity of a nickel concentration of 80%. A disadvantage of permalloy is that it is not very ductile or workable, so applications requiring elaborate shapes, such as magnetic shields, are made of other high permeability alloys such as mu metal. Permalloy is used in transformer laminations and magnetic recording heads.

Ohmalloy-1J79 widely used in radio-electronic industry, precision instruments, remote control and automatic control system.

Ohmalloy 1J79 / Permalloy strip for Relays and Core

Normal composition%

Ni	78.5~80.0	Fe	Bal.	Mn	0.6~1.1	Si	0.3~0.5
Mo	3.8~4.1	Cu	≤0.2
C	≤0.03	P	≤0.02	S	≤0.02

Typical Physical properties

Density (g/cm3)	8.6
Electrical resistivity at 20(mm²/m)	0.55
Coefficient of linear expansion(20~200)X10^-6/	10.3~11.5
Saturation magnetostriction coefficient λ_θ/ 10^-6	2.0
Curie point T_c/	450

The magnetic properties of alloys with high permeability in weak fields
1J79	Initial permeability	Maximum permeability			Coercivity	Saturation magnetic induction intensity
old-rolled strip/ sheet. Thickness, mm	μ_0.08/ (mH/m)		μ_m/ (mH/m)	Hc/ (A/m)			B_S/ T
	≥			≤
0.01 mm	17.5		87.5	5.6			0.75
0.1~0.19 mm	25.0		162.5	2.4
0.2~0.34 mm	28.0		225.0	1.6
0.35~1.0 mm	30.0		250.0	1.6
1.1~2.5 mm	27.5		225.0	1.6
2.6~3.0 mm	26.3		187.5	2.0
cold drawn wire
0.1 mm	6.3		50	6.4
Bar
8-100 mm	25		100	3.2

Heat treatment 1J79
Annealing media	Vacuum with a residual pressure not higher than 0.1Pa, hydrogen with a dew point of not higher than minus 40 .
The heating temperature and rate	1100~1150
Holding time	3~6
Cooling rate	With 100 ~ 200 / h cooled to 600 , rapidly cooled to 300